Cathodic electrode

ABSTRACT

A polymer bonded sheet product suitable for use as an electrode in a non-aqueous battery system wherein the electrode is a microporous sheet composed of from 2-30 weigth percent polyethylene, 70-98 weight percent of electrically conductive and electrochemically active particulate material and from 0 to 5 weight percent of a plasticizer for the polyethylene.

This application is a continuation-in-part application of U.S. application having Ser. No. 384,854, filed Jul. 21, 1989, (abandoned), which is a continuation application of U.S. application having Ser. No. 85,330, filed Aug. 14, 1987, (matured to U.S. Pat. No. 4,853,305) which is a continuation application of U.S. application having Ser. No. 843,347 filed Mar. 24, 1986 (abandoned).

BACKGROUND OF THE INVENTION

The present invention is directed to polymer bonded electrodes useful in a non-aqueous battery and to a battery system containing said electrodes.

Storage batteries have a configuration composed of at least one part of electrodes of opposite polarity and, generally, a series of adjacent electrodes of alternating polarity. The current flow between electrodes is maintained by an electrolyte composition capable of carrying ions across electrode pairs.

Non-aqueous batteries have certain distinct advantages over other types of storage batteries. They use, as anodes, light weight or alkali metals, such as lithium, lithium-aluminum alloys, lithium-carbon composites and the like which are at the far end of the electromotive series. Those batteries have the potential for providing much higher gravimetric and volumetric energy densities (capacity per unit weight and volume, respectively) than other types of batteries due to the low atomic weight of the metal and high potential for forming a battery in conjunction with suitable positive electrodes far removed from the light weight (alkali) metal electrode (the description herein will use batteries having lithium as the light weight metal anode although other light weight metals can be used) in the electromotive series. The battery can be formed in any conventional physical design, such cylindrical, rectangular or disc-shaped "button" cells, normally of a closed cell configuration.

The battery components of positive electrode, negative electrode and separator can be in the form of distinct alternating plates in a sandwich design or of a continuous spirally wound design as are well known. The anodic electrodes can be formed, for example, from lithium metal or its alloys on a support, such as a nickel coated screen. The electrolyte can be formed of a non-aqueous solvent or fused or solid electrolyte. Illustrative of known useful non-aqueous solvents include acetonitrile, tetrahydrofuran and its derivatives, propylene carbonate, various sulfones, and mixtures of these solvents containing a light metal salt such as lithium salts, as for example, lithium perchlorate, iodide or hexafluoroarsenate and the like. An additional, normally passive component of the battery is a separator membrane located between plates of opposite polarity to prevent contact between such plates while permitting electrolytic conduction. Separators are normally of the form of sheets which possess very low electronic conductivity.

Significant developments have been made in the fabrication of non-aqueous batteries. However, one of the major concerns is the lack of development of a suitable electrode in which the electrochemically active material is present in the form of a porous, flexible, sheet material. The active material must be bonded into a unitary sheet by a material which is inert with respect to the other components of the battery as well as being inert and compatible to the active material. The bonding material must be capable of readily forming a uniform sheet. The resultant sheet must have the active material uniformly distributed through the length and breadth of the sheet as well as across its thickness to provide maximum effectiveness. The bonding material must be kept to very low amounts of the total sheet material or the active material will be encompassed by the bonding material and thereby dramatically reduce the conductivity and activity of the resultant electrode sheet product. Even though present in only small amounts the bonding polymer must be capable of maintaining the sheet integrity and provide resistance to fractures, spalling and disintegration attributable to the expansion and contraction forces encountered in charge-discharge cycling.

Polymer bonded electrodes presently known have a number of deficiencies which has limited their utility and, thereby limited the acceptance of an effective non-aqueous battery system. The presently known polymer-bonded electrodes are not capable of being mass produced by a reliable, cost-effective, non-aqueous process. In addition, the majority of known polymer-bonded electrodes exhibit flaking and disintegration when the formed free-standing sheet is further processed, such as when applied to a current collector and/or during assembly into a battery.

A number of bonding polymers have been considered for and used in the fabrication of cathodic polymer bonded electrodes. The most widely used material at the present time is poly(tetrafluoroethylene), commonly referred to as PTFE or by the tradename Teflon. PTFE bonded electrodes have certain drawbacks which limit their usefulness and ability to provide a highly effective product. For example, the chemical inertness of this polymer causes the fabrication of electrodes to be both difficult and laborious. Generally, it requires initially mixing the active material with an aqueous slurry of PTFE which is then doctored onto a surface and heated to high temperatures (250°-400° C.) to remove the water and cause bonding. The presence of water and the processing at high temperatures limits the active materials which can be used in forming the electrode product. For example, certain chalcogenides are known to be unstable in the presence of water. PTFE bonded sheets tend to flake and are not free standing unless large amounts of polymer are used. The sheets are conventionally bonded to a current collector screen by pressing them together at high temperatures. This process normally produces a brittle product which tends to crack and chip. Finally, a major defect of this known class of product is its non-uniformity both in distribution of active material and of porosity. This defect is inherently due to the processing techniques required, especially the evaporation of solvent from the materials causing non-uniformity across its thickness as well as from point-to-point on the sheet product. Patents illustrating formation of polymer bonded electrodes by this technology are U.S. Pat. Nos. 3,457; 3,407,096; and 3,306,779.

Some work has been done to form a product from dry tetrafluoroethylene suspensions to overcome the incompatibility problems associated with water but such products require sintering at very high temperature (e.g. 400° C.) which also limits the types of active fillers which can be used. Patents illustrating this known technology are U.S. Pat. Nos. 20 3,184,339 and 3,536,537.

Most recently polymer bonded electrodes have been formed from slurries of EPDM (ethylene-propylene-diene terpolymer) in an organic medium, such as cyclohexane (see "Elastomic Binders for Electrodes" by S.P.S. Yen et al., J. Electrochem. Soc., Vol. 130, No. 5, pg. 1107). Other elastomeric polymers, such as sulfonated ionomers, butyl rubbers and the like have also been used in forming electrodes by a slurry technique (See U.S. Pat. No. 4,322,317). The resultant electrode products formed in this manner exhibit greater elasticity and compatibility with the other battery components. However, the defects of non-uniformity of product, poor control of porosity and pore size distribution remain a problem. In addition, electrodes made by this method exhibit severe loss of activity after being subjected to only a few charge/discharge cycles as noted by the low figure of merit reported in U.S. Pat. No. 4,322,317.

It is highly desirable to be able to provide a polymer bonded electrode which is capable of being readily fabricated without being labor intensive. Further, it is desired to provide a polymer-bonded electrode which can be formed with a very high content of electrochemically active particulate material, can exhibit a high degree of uniformity, is a flexible material which can be readily formed into desired configuration, can maintain its integrity under the conditions encountered in a battery (including expansion-contraction of cycling) and can be initially formed into a free-standing sheet product which can be readily adhered to a current collector element, such as an expanded metal grid or wire screen. Finally, it is highly desired to provide a polymer-bonded electrode which is in the form of a sheet of controlled microporosity capable of permitting entry and mobility of electrolyte therein which can thereby increase the electrode's activity.

Upon initial consideration, it might be assumed that many binding materials could be used as alternatives to the small number of materials presently used and obtain the desired results. However, although there are a large number of polymers available as binders in many applications including as electrode binders, a selection of a specific binder is not obvious to the artisan when attempting to provide a chalcogenide filled cathodic electrode because of the many factors which influence the results one obtains with any particular binder. Among the major factors which influences the results obtained are: (1) the solubility of the binder in the organic electrolytes which are required in this application; (2) the chemical stability of the polymer at the electrode potential realizing that many cells are operated at different potentials; (3) the stability of the electrochemically active and electrically conductive materials used in combination with a particular binder and under the conditions needed for fabrication; (4) the ability of the polymer to bind the particulate material into a unitary structure at very low concentrations in order to provide a cathodic electrode with good performance; (5) the ability and ease of obtaining a uniform distribution of the binder with the active material of the electrode; (6) the ability of the polymer to maintain a stable electrode capable of undergoing a multiplicity of charge-discharge cycling; (7) the number and ease of steps required to obtain the desired cathodic electrode; and (8) the safety, availability of material and cost. Thus, selection of a polymer for use in forming a high performance electrode containing metal chalcogenides has been a difficult task because of the above factors which impose severe restrictions and limitations.

It has now been discovered that a cathodic polymer bonded electrode suitable for use in non-aqueous batteries can be readily formed in a manner which provides a superior electrode and overcomes the processing problems associated with Teflon and other presently used polymers as described above.

SUMMARY OF THE INVENTION

The present invention is directed to a polymer bonded electrode and to a non-aqueous battery system containing said electrode product in which the electrode is a thin, microporous sheet composed of from 2-30 weight percent polyethylene, 70-98 weight percent of particulate material composed of electrochemically active and electrically conductive materials and from 0-5 weight percent of an organic plasticizer for the polyethylene. The sheet is prepared by forming a substantially uniform mixture of the components with from 20 to 60 volume percent excess of plasticizer, shaping the mixture into a free-standing sheet and extracting substantially all of the plasticizer therefrom. The resultant product is a flexible sheet material which possess a high degree of mechanical integrity, strength and uniformity, has a controlled pore volume with pore size of narrow distribution and exhibits high conductivity of at least 0.1 reciprocal ohm-cm and preferably at least 0.3 reciprocal ohm-cm.

The polymer bonded electrode product formed according to the present invention is capable of exhibiting high degree of activity even after subjection to a large number of charge/discharge cycles.

DETAILED DESCRIPTION OF THE INVENTION

The polymer bonded electrode product of the present invention is in the form of a thin sheet which is required to be formed from a homogeneous admixture of polyethylene, a plasticizer for the polyethylene, and particulate material having a combination of electrochemical active and electrically conductive properties as are described herein below.

The polymer electrode product of the instant invention is formed through a series of precursor materials. Generally, a uniform admixture is initially formed of polymer, plasticizer and particulate material. The admixture is capable of exhibiting sufficient flow and rheological characteristics to permit the admixture to be readily processed and shaped to relatively low temperatures (i.e. 25° C.-170° C.). An initial free-standing sheet is formed from the admixture. The plasticizer component is then removed from the initial sheet. This removal normally occurs subsequent to the forming of a laminate in which a metal screen (a current collector) is laminated to a sheet or sandwiched between two sheets to provide an electrode product. The final electrode product, having had the plasticizer component substantially removed, is a highly filled (normally 85 wt%. or greater) product useful as a polymer bonded electrode.

The present invention requires the utilization of polyethylene of medium or high density [high density (about 0.96) is preferred]. Although homopolymers are preferred, the term "polyethylene", as used herein and in the appended claims, shall mean polyethylene homopolymers and copolymers in which copolymer is formed from olefinic monomers such as ethylene, propylene, butene-1, acrylate and the like with the major (preferably at least 80 percent) olefinic monomer being ethylene.

The polyethylene should be of high molecular weight having a weight average molecular weight of at least about 150,000 and is preferably selected from higher molecular weights such as from about 200,000 to 5,000,000. The preferred polyethylenes are homopolymers of high molecular weight such as of a weight average molecular weight of 200,000 to 5,000,000 and most preferably from 250,000 to 5,000,000. The polymer component used in forming the subject electrode product can be comprised of a mixture of a high molecular weight polyethylene and a minor amount of low molecular weight polyethylene. The mixture can be formed from about 50 to 99 weight percent of a high molecular weight polymer and a corresponding 1 to 50 weight percent of a low molecular weight polymer. The term "high molecular weight polymer" is intended to refer to a polymer having a weight average molecular weight of at least 250,000 and "low molecular weight polymer" refers to a polymer having a weight average molecular weight of from about 100,000 to 250,000. The amount of low molecular weight polymer which may be present as part of the mixture of polymers is directly dependent on the molecular weight of the high molecular weight polymer component.

The plasticizer of the instant composition must be present in the initial formulating and processing to form an initial sheet product, as more fully described below. The plasticizer provides the means of fabricating the composition to a uniform consistency and to aid in inducing and controlling the degree of porosity, the pore size distribution and uniformity of porosity throughout the resultant sheet product.

Plasticizer suitable for the instant invention are compounds which are capable of plasticizing polyethylene at least under the formulation and processing conditions used to form the initial sheet product, are substantially inert with respect to the particulate material used herein, and are substantially soluble in an organic solvent which is a non-solvent with respect to the polymer component described above and the particulate material described below which are used in forming a particular composition. Representatives of such plasticizers are organic esters, such as sebacates, phthalates, stearates, adipates and citrates; epoxy compounds such as epoxidized vegetable oil; phosphate esters such as tricresyl phosphate; hydrocarbon materials such as petroleum oil including lubricating oils and fuel oils, hydrocarbon resin and asphalt and pure compounds such as eicosane; coumarone-indene resins and terpene resins; tall oil and linseed oil. The preferred plasticizers are hydrocarbon materials and most preferred plasticizers are selected from petroleum oils. The plasticizer is generally substantially free of water (anhydrous) and, therefore, compatible with the subject battery system.

The organic plasticizer used herein aids in fabricating the sheet product and in imparting microporosity to the resultant sheet. The void volume of the resultant sheet will be directly dependent upon the amount of plasticizer used to form the initial composition and the amount of plasticizer extracted to provide the final sheet product. Void volumes of the final sheet product may range from about 15 volume percent to about 60 volume percent with from about 25 to 40 volume percent being preferred. Higher ranges are normally acceptable for sheet products having higher cross-sectional dimensions. The sheet's void volume is of a microporous character which generally have narrow distribution and are of low mean diameter (i.e. 0.05 to 0.5 microns) and can be determined by standard mercury intrusion techniques.

The particulate material required in forming the present admixture and the resultant sheet is composed of electrochemically active (normally cathodic on discharge in secondary battery systems) and electrically conductive materials. They must be in particulate form. Smaller particle size material (such as a mean particle size of about 25 microns or less and preferably less than 10 microns) is preferred to enhance intimate contact between the particles of electrochemically active material contained in the resultant electrode. The term "electrochemically active" refers herein and in the appended claims to the ability of a material to enter and participate in a redox reaction during the operation and in the environment of an electrochemical cell. The term "electrically conductive" refers herein and in the appended claims to the ability of a material to exhibit low resistance to electron transfer. The particulate material used herein will normally require a mixture of materials selected from the chalcogenide compounds described below and from electrically conductive diluent also described below. The combination of materials should be such as to provide an electrode sheet product capable of exhibiting an overall conductivity of at least about 0.1 reciprocal ohm-cm. When the electrochemically active material is also sufficiently electrically conductive, to provide the desired overall conductivity, it may be used alone. When the cathodically-active material has low electrical conductivity (the majority of the chalcogenide exhibit less than about 0.001 reciprocal ohm-cm) they will be used in combination with conductive diluent as described below.

The electrochemically active and electrically conconductive particulate material can be one or more of the chalcogenide compounds selected from sulfides, oxides, selenides, and tellurides of titanium zirconium, hafnium, niobium, copper, iron, tantalum, chromium, cobalt, nickel, manganese and vanadium. In general, such chalcogenides contain about 1.8 to about 3.2 atoms of the chalcogenide per metal atom. Advantageously, when forming a secondary battery the cathodic electrode is preferably selected from a chalcogenide of cobalt, nickel, titanium and/or vanadium and most preferably titanium sulfides or, oxides of cobalt, manganese or vanadium. When forming a primary battery, the preferred chalcogenides are formed from vanadium, such as V₂ O₅, iron and copper especially the sulfides of iron and copper. Also, among the chalcogenides, those which contain about 1.8 to about 2.1 atoms of chalcogen per metal atom, commonly referred to as the dichalcogenides, are preferred.

Examples of cathode-active materials which may be useful and which are selected from the above-mentioned chalcogenides are zirconium disulfide, hafnium disulfide, niobium triselenide, tantalum disulfide, vanadium disulfide, vanadium diselenide and vanadium ditelluride as well as vanadium oxide such as V₃ O₈ and V₅ O₁₃. Also includes are the chalcogenides having more than one of the mentioned metals, e.g., V₀.25 Ti₀.75 S₂.0 and vanadium iron disulfide. Also included are those chalcogenides having metals other than those described above, such as intercalation (also known as insertion) compounds wherein the intercalation metals (such as alkali metal, preferably lithium or sodium used to form the anode) replace a portion or insert into the structure of the cathodic chalcogenide (e.g. lithium cobalt oxides, lithium manganese oxides, lithium cobalt-nickel oxide and the like). Lastly, it should be noted that while the trichalcogenides and dichalcogenides are described, the present invention is not limited thereto and may include, for example, the pentachalcogenides and the like.

The particulate material may further comprise minor amounts (up to about 30 weight percent) of conductive diluent such as high surface area conductive carbon black. The diluent is normally of ultrafine particle size of from about 1 to 100 millimicrons and have a (BET) surface area of at least 40 m² /g and preferably from 7 to 2000 m² /g. The carbon can serve several roles to enhance the subject electrode. In instances where the particulate chalcogenide used has good electronic conductivity, the carbon merely acts as an electrical conductive bridge between particles of chalcogenide to further enhance the total properties of the resultant electrode. Where the chalcogenide has poor electronic conductivity i.e. V₂ O₅ (high resistance) the conductive diluent provides a means for carrying the electron to the current collector from the electrochemically active chalcogenide site.

In addition to the above described components, the initially formed admixture may further contain conventional stabilizers, antioxidants, wetting agents, processing aids or mixtures thereof. Representative of stabilizers are 4,4-thiobis(6-tertbutyl-m-cresol) sold commercially under the tradename "Santonox" and 2,6-ditert-butyl-4-methylphenol sold commercially under the tradename "Ionol". Examples of known commercially available wetting agents include sodium alkyl benzene sulfonate, sodium lauryl sulfate, dioctyl sodium sulfosuccinate, and isoctyl phenyl polyethoxyethanol. Processing aids include stearates, graphite and the like.

The above-described components can be readily formed into a substantially homogeneous admixture. The initial admixture should be formed by blending from about 5 to 35 (preferably 5-20) volume percent polymer, from about 25 to 75 (preferably 40 to 60) volume percent of particulate material and from about 20 to 50 volume percent of polymeric plasticizer.

The blending of the components can be readily accomplished by conventional means such as by initially mixing at room temperature in a blender and then in a Banbury, Brabender or sigma blade mixer or the like at moderate (about 25° to about 170° C., preferably from about 120° to about 160° C.) temperatures. The blending and processing is preferably done under dry conditions to avoid water pick-up by the materials.

It has been found that extremely high particulate content admixtures required by the present invention exhibit rheological properties which permit them to be readily shaped and formed into thin free-standing sheet products of less than about 50 mils, preferably less than about 20 mils. It must be understood that the particular thickness can be customized by the artisan based on the battery design and its acceptable drain rate. Sheet products and electrodes therefrom can be made of less than 5 mils and even less than 3 mils thickness. Sheet products made by presently known conventional techniques can not be formed of such thin dimensions and maintain good mechanical properties as is attainable by sheet products of the present invention. The term "sheet" as used herein and in the appended claims refers to a shaped product having extensive length and breath dimensions and of thin cross-section and which may have major surfaces which are substantially flat or of a predetermined design. The initial sheet can be readily formed from the admixture by subjecting the admixture to extrusion, calendering, injection molding or compression molding processing. All of these processing means are capable of producing the initial sheet in large volume using low labor involvement. The most preferred method is extrusion of the admixture using a conventional extrusion apparatus to continuously provide initial sheet product.

The forming of the initial sheet (a sheet having high levels of plasticizer therein) can be readily accomplished at moderate operating conditions, including low temperature of from about 25° to 175° C. and preferably from about 120° to 160° C. Such temperatures allow formation of sheet product using components normally deemed unsuitable under known slurry processes. Further the present process provides a sheet which is freestanding and has substantial uniform distribution of particulate material throughout its length and breadth dimensions as well as across its cross-sectional dimension.

The initially formed sheet can be readily made into a suitable cathodic electrode by laminating a conventional current collector with at least one sheet of the present invention. The plasticizer component can be extracted, as described below, prior or subsequent to lamination with the current collector. It is preferred to initially form the laminate structure of at least one sheet with a suitable current collector and then extract the plasticizer material.

The current collector is normally a screen, grid, expanded metal, woven or non-woven fabric or the like formed from efficient electron conductive materials such as carbon, or metals such as copper, aluminum, nickel, steel, lead, iron or the like. The current collector, when laminated to the final sheet product (a sheet substantially comprising particulate material bonded by very low amounts of polyethylene) of the present invention, provides a low electronic resistance path between the active material and the battery terminal.

The formed electrode sheet, with or without the presence of plasticizer, is a pliable and moldable material which can be readily laminated to the collector screen by concurrently passing a screen and at least one sheet through a set of nip rollers or the like to press (under low pressure and preferably at moderate temperatures of about 25° to 170° C.) to produce a laminate product. It is preferred that the laminate be of a configuration of a screen sandwiched between (and thereby embedded in) two sheets although a laminate of a single sheet and single screen may be desired in certain applications. The laminate can be most readily formed by utilizing an initial sheet product immediately after its production to utilize the sheet in its elevated temperature state.

The plasticizer contained in the initial formed sheet should be substantially completely removed, such as by means of extraction using suitable solvent. The composition of the resultant electrode will depend upon the degree of extraction of the plasticizer. The plasticizer can be substantially completely removed, leaving a microporous polymeric sheet product which is highly filled with cathodic active material. The resultant sheet product exhibits good physical properties and a high degree of microporosity. The exact degree of microporosity is induced and regulated to a large degree by the amount of plasticizer used and extracted. The microporosity character of the resultant polymer bonded electrode provides a means to permit the electrolyte to be in intimate contact with a very high percentage of the particulate material. It is believed, although not meant to be a limitation on the present invention, that the microporous structure of the sheet permits the particles residing in the interior of the sheet to be more active, that is to be more active in the electrochemistry of the battery system.

The procedure for extraction of the plasticizer from a sheet product is well known and is not meant to form a part of the present invention, per se. A single stage extraction can be used. The solvent or extraction conditions should be chosen so that the polyolefin and particulate material are essentially insoluble. For example, when petroleum oil is to be extracted from the formed sheet, the following solvents are suitable; chlorinated hydrocarbons, such as trichloroethylene, tetrachloroethylene, carbon tetrachloride, methylene chloride, tetrachloroethane, etc., as well as hydrocarbon solvents such as hexane, benzene, petroleum ether, toluene, cyclohexane, gasoline, etc. Generally, aqueous solvents should not be used as these would attack most of the required filler components.

The extraction temperature can range anywhere from room temperature up to the melting point of the polyolefin as long as the polyolefin does not dissolve. The temperature can be maintained such that all components remain stable and are not adversely effected.

The time of the extraction will vary depending upon the temperature used and the nature of the plasticizer or filler being extracted. For example, when a higher temperature is used, the extraction time for an oil of low viscosity can be a very short time of up to only a few minutes, whereas if the extraction is performed at room temperature, the time requirement will be greater.

The final composition of the polymer-bonded electrode sheet product will depend upon the original composition and the degree of extraction of the plasticizer from the sheet product. The extracted sheet normally has from about 2 to 30 weight percent polyethylene, about 70 to 98 weight percent particulate material, and from about 0 to 5 weight percent plasticizer. The more preferred electrode comprise a mixture of from 4 to 15 weight percent polyolefin, 85 to 96 weight percent particulate material, and from 0 to 3 weight percent plasticizer.

In a preferred embodiment, 12 volume percent polyethylene, 53 volume percent particulate material, and 35 volume percent plasticizer are blended together, extruded to provide a flat sheet and then sufficient plasticizer is extracted to provide a finished electrode sheet composed of 18 volume percent polyolefin, 81 volume percent particulate material, and 1 weight percent plasticizer.

The porosity volume percents or void volume percent were calculated for the resultant sheet product by calculating the wet weight minus dry weight divided by the sheet product's geometric wet volume.

Charge/Discharge cycling was performed on cells having the subject sheet using a Princeton Applied Research Model 363 galvanostat. The galvanostat was powered and monitored with an Analog Devices μMAC 5000 microcomputer which controlled the current passing through the cell and measured the current voltage and charge throughout the cycle.

The electrical conductivity of the resultant sheet product were measured with a Yellow Spring Instrument Conductivity Bridge at 1 KHz by placing a nickel metal clamp on each of the two opposite ends of the specimen to be tested in such a manner as to have a free sample spacing of 1 cm by 1 cm not covered by the clamps. The thickness of the samples were measured. The clamps were connected to a conventional conductivity bridge and the resistance of the samples were measured. The clamps were adjusted to a spacing of 2 cm by 1 cm and the resistance measured.

The following examples are given for illustrative purposes only and are not meant to be a limitation on the subject invention, except as made in the claims appended hereto. All parts and percentages are by weight unless otherwise indicated.

EXAMPLE 1

Eight parts of high density polyethylene of a weight average molecular weight of 250,000 were mixed with 22 parts of hydrocarbon oil (Sunthene 255; density of 0.89 g/ml, 54 ssu at 210° F., flash point of 390° F.), 19 parts of Shawinigan processed carbon black (acetylene black, 50% compressed density of 2.1 gm/cc, 70 m² /gm BET surface area) 3 parts of graphitic carbon (density of 2.1 gm/cc 5 m² /gm BET surface area) and 54 parts of minus 200 mesh V₂ O₅ (Cerac). The mixture was placed in a Brabender blender maintained at a temperature of 150° C. and mixed for about 5 minutes until steady torque is obtained. A dry nitrogen atmosphere was maintained over the equipment.

A sample of the resultant composition was hot pressed at a pressure of about 250 psi at a temperature of 150° C. for approximately 10 seconds to produce a uniform sheet of 18 mil thickness. The formed sheet was then immersed in cyclohexane for 3 periods of 10 minutes each to yield a microporous sheet having 36 percent void volume substantially uniformly distributed throughout. The composition of the extracted, microporous sheet was 9.5 percent polyethylene, 26.2 percent combined particulate carbon 64 percent V₂ O₅ and less than 1 percent oil. The electronic conductivity of the microporous sheet measured at 22° C. and 1 KHz and 0.11 ohm⁻¹ cm⁻¹.

EXAMPLE 2

A cathodic electrode was formed with the composition of Example 1 above and the electrode was used as part of a LiV₂ O₅ battery cell. Two sheets (approx. 3 mils each) were formed by pressing samples of the composition of Example 2 above at 150° C. and 250 psi. The sheets were placed on each side of an expanded nickel metal screen and the composite subjected to pressure of 250 psi at 150° C. for approximately 10 seconds to produce a product having the screen embedded therein. An examination of the product showed that the polymeric sheets had formed into a single unitary structure. The product was immersed in cyclohexane bath for 3 periods of 10 minutes each to yield a microporous polymer bonded electrode product. The electrode was then dried at 10-20 microns vacuum and 80° C. for 2 hours to remove residual amounts of solvent. The formed cathodic electrode was placed in an Argon atmosphere glove box for assembly as part of a cell with a lithium foil of 1 cm² and 5 mil thickness which had been pressed onto a commercially available expanded nickel metal grid. The two electrodes were placed into rectangular glass tubing using a commercial polypropylene microporous sheet separator between the electrodes. The cell was filled with 0.5 ml 1.2M LiAsF₆ in 2-methyltetrahydrofuran. The cell was then temporarily sealed with an O ring, taken out of the glove box and permanently glass sealed in a flame.

The cell contained 13.1 mg V₂ O₅ which is equivalent to a theoretical capacity of 4.1 mAH (assuming the discharged material is Li₂ V₂ O₅). The cell was discharged at 2 mA to a cutoff voltage of 3.0 volts. Capacity utilization at 1 mA was 100% for Cycle #1, 65% for Cycle #3, 37% for Cycle #14 and 36% for Cycle #30. Because of the high theoretical capacity of this V₂ O₅ electrode system, the charge density was still very high even at the relatively low capacity percentage obtained.

EXAMPLE 3

Eight parts of high density polyethylene of a weight average molecular weight of 250,000 were mixed with 22 parts of hydrocarbon oil (Sunthene 255; density of 0.89 g/ml, 54 ssu at 210° F., flash point of 390° F.), 19 parts of Shawinigan processed carbon black (acetylene black, 50% compressed, 3 parts graphitic carbon and 65 parts of FeS₂ (Cerac; minus 100 mesh, 99.9 percent purity). The mixture was processed in the same manner as described in Example 1 above. The composition of the formed sample of extracted microporous sheet product was: 8 percent polyethylene, 27 percent combined carbons and 65 percent FeS₂. The oil content was negligible. The electronic conductivity of the formed microporous sheet measures at 1KHZ and 22° C. was 0.6 ohm⁻¹ cm⁻¹.

A Li-FeS₂ cell was fabricated by the same procedure as described in Example 2 above using the polymer FeS₂ composition of this example. The cell contained 12.9 mg of FeS₂ (active material, a 5 mil Li foil and approximately 0.5 ml of an electrolyte solution composed of 1M LiClO₄ in propylene carbonate. The cell was tested by conventional charge-discharge cycling procedure discharged at 1 mA to a cutoff voltage of 1 volt and charged at 0.25 mA to a voltage limit of 2.5 volts. The cell delivered 7 mAh in Cycle #1, 5.3 mAH in Cycle #4, and 3.9 mAH in Cycle #6. The theoretical capacity based on 2 electrons per iron atom is 5.8 mAh.

EXAMPLE 4

The procedure described in Example 3 above was repeated except that the amount of carbon black was reduced to 18 parts and the amount of FeS₂ was increased to 80 parts. The formed extracted sheet was composed of 7 percent polyethylene, 19 percent combined particulate carbons, 73 percent FeS₂ and less than 1 percent oil The electronic conductivity of the sheet, measured at 1 Khz and 22° C. was 0.4 ohm⁻¹ cm⁻¹. A FeS₂ electrode was made according to the procedure of Example No. 2 and a LiFeS₂ cell was fabricated as described in Example No. 3. This cell contained 15.3 mg of FeS₂. The cell was discharged at 1 mA, and charged at 0.5 mA to 2.5 volts. The cell delivered 3.8 mAh to 1.3 volts over 5 charge/discharge cycles.

EXAMPLE 5

The procedure of Example 1 was repeated using a mixture of components composed of 9 parts of high-density polyethylene of weight average molecular weight of 250,000, 21 parts hydrocarbon oil (Sunthene 255) and 104 parts of CuS (Cerac; minus 200 mesh, 99.5 percent purity). The formed extracted microporous sheet was composed of about 8 percent polyethylene, 92 percent CuS and residual oil. Conductivity of the sheet, measure at 1 Khz and 22° C. was 3.3 ohm⁻¹ ch⁻¹.

A Li-CuS cell was fabricated using the material of this Example according to the procedure described in Example 2. The cell which contained 18.6 mg of CuS was discharged at 2 mA to 1.3 V and charged at 1 mA to 2.5 V. The maximum capacity obtained on discharge was 5.4 mAh which is equivalent to 1.03 Li ions per copper atom.

EXAMPLE 6

A cathodic electrode was formed by dry blending 5.6 parts of high density polyethylene having a weight average molecular weight of 250,000, 18.4 parts hydrocarbon oil (Sunthene 255) 12 parts of Shawinigan processed carbon black, 1.6 parts of graphitic carbon and 62.4 parts of lithium cobalt oxide particulate of minus 325 mesh. The mixture was compounded at 160° C. using a Brabender compounder. A portion of this material was hot pressed into a commercially available aluminum expanded metal current collector to form an 8 cm×4 cm×12 mil thick electrode containing 0.87 g. LiCoO₂.

The cathode sheet was used to form an electrochemical cell. The formed cathode sheet was wound into a jelly roll configuration with a sheet of microporous polypropylene (Celgard 2500) and a lithium foil 10.5 cm×4 cm×7 mil thick. The cell was filled with 2.3 ml of electrolyte consisting of 2M LiAsF₆ and 0.4M LiBD₄ in 80/20 mixture of methyl formate and dimethyl carbonate. The cell was sealed and tested by cycling under the regimen of charging at 0.5 mA/cm² to 4.5 volts and then discharging at 1 mA/cm² to 3.0 volts. The test was discontinued after 160 cycles. 

We claim:
 1. An electrode suitable for use in a non-aqueous battery system comprising at least one microporous sheet capable of being a free-standing sheet composed of a substantially homogeneous composition of from about 70-98 weight percent of electrochemically active and electrically conductive particulate material composed of at least one metal chalcogenide having a metal selected from titanium, zirconium, hafnium, niobium, copper, iron, tantalum, vanadium, manganese, chromium, cobalt, nickel and mixtures of said metals alone or together with intercalated metals, said particulate material has up to about 30 weight percent of a conductive carbon particulate having an average particle size of from about 1 to 100 millimicrons, from about 2-30 weight percent of polyethylene having a weight average molecular weight of from 150,000 to about 5,000,000 and from 0 to about 5 weight percent of an organic plasticizer for said polyethylene; and a current collector composed of a conductive material, said collector being in intimate contact with each of said at least one microposous sheet.
 2. The electrode of claim 1 wherein the polyethylene is high density polyethylene having a weight average molecular weight of from 200,000 to 5,000,000.
 3. The electrode of claim 1 wherein the polyethylene is composed of a major amount of a polyethylene having a weight average molecular weight of at least 250,000 and a minor amount of a polyethylene having a weight average molecular weight of from about 100,000 to 250,000.
 4. The electrode of claim 1 wherein the metal chalcogenide has a metal selected from titanium, cobalt, manganese, nickel, and vandium.
 5. The electrode of claim 1 wherein the metal chalcogenide has a metal selected from iron, copper and vanadium.
 6. The electrode of claim 1, 2, 3, 4, or 5 wherein the metal chalcogenide is intercalated with an alkali metal selected from lithium or sodium.
 7. The electrode of claim 1, 2, 3, 4 or 5 composed of two sheets having the current collector therebetween.
 8. The electrode of claim 6 composed of two sheets having the current collector therebetween.
 9. In a secondary non-aqueous battery comprising at least one pair of electrodes composed of an anodic electrode and a cathodic electrode, and a non-aqeuous electrolyte composition, said anodic electrode formed from an alkali metal, alkali metal alloy or alkali metal-carbon composite wherein the improvement comprises having the cathodic electrode consist essentially of the product of claim 1, 2, 3, or 4 in which the metal of the metal chalcogenide contained therein is selected from titanium, zirconium, hafnium, niobium, tantalum, chromium, cobalt, nickel, vanadium, mixtures and intercalated products thereof.
 10. The secondary battery of claim 9 wherein the cathodic electrode is composed of two sheets having a current collector therebetween.
 11. The secondary battery of claim 9 wherein the metal chalcogenide is intercalated with an alkali metal selected from lithium or sodium.
 12. In a primary non-aqueous battery comprising at least one pair of electrodes composed of an anodic electrode and cathodic electrode and a non-aqueous electrolyte composition, said anodic electrode formed from an alkali metal, alkali metal alloy or alkali metal carbon composite, wherein the improvement comprises having a cathodic electrode consisting essentially of the product of claim 1, 2, 3, or 4 in which the metal of the metal chalcogenide contained therein is selected from vanadium, iron, copper, manganese or mixtures thereof.
 13. The primary battery of claim 12 wherein the cathodic electrode is composed of two sheets having a current collector therebetween. 